Effect of Deposition Temperature on the Phase Transition of Ti, Al, C and Related Properties of the Graphite-Like Carbon Film

Ke Li,Yanxia Wu, Yanjie Xu, Shengwang Yu,Jie Gao,Ying Liu

WEAR（2025）

Cited 0|Views1

Abstract

The graphite-like carbon films contained Ti and Al elements were prepared by magnetron sputtering at different deposition temperatures and the structure, corrosive as well as tribological properties in different environments with ZrO2 as counterpart balls were investigated. The results revealed that the sp3C content in the film first increased and then decreased, the Ti, Al elements in the films changed from TiC nanocrystals to Ti3AlC with increasing temperature. Specially, there were totally Ti3AlC with an ant-perovskite phase at 350 degrees C. Consequently, the film contained Ti3AlC phase showed better corrosive resistance compared to that contained TiC phase, due to the TiC nanocrystal reduced the migration barrier and penetration energy of Cl ions in the corrosion medium, which accelerated the process of corrosion failure. It was noteworthy that the film prepared at 350 degrees C showed better corrosion resistance due to its higher sp3C content, higher hydrophobicity, higher adhesion strength, lower residual internal stresses, and lower film porosity. All the film exhibited better tribological properties in 3.5 wt% NaCl solution than in air related to the water lubrication. Especially, owing to the synthesis effect of TiC and Ti3AlC phase, the film prepared at 300 degrees C showed better tribological properties.

Translated text

Key words

Magnetron sputtering,Graphite-like carbon films,Ti and Al elements,Corrosion,Tribological properties

求助PDF

上传PDF

Bibtex

AI Read Science

AI Summary

AI Summary is the key point extracted automatically understanding the full text of the paper, including the background, methods, results, conclusions, icons and other key content, so that you can get the outline of the paper at a glance.

Example

Background

Key content

Introduction

Methods

Results

Related work

Fund

Key content

Pretraining has recently greatly promoted the development of natural language processing (NLP)
We show that M6 outperforms the baselines in multimodal downstream tasks, and the large M6 with 10 parameters can reach a better performance
We propose a method called M6 that is able to process information of multiple modalities and perform both single-modal and cross-modal understanding and generation
The model is scaled to large model with 10 billion parameters with sophisticated deployment, and the 10 -parameter M6-large is the largest pretrained model in Chinese
Experimental results show that our proposed M6 outperforms the baseline in a number of downstream tasks concerning both single modality and multiple modalities We will continue the pretraining of extremely large models by increasing data to explore the limit of its performance

Upload PDF to Generate Summary

Must-Reading Tree

Example

Generate MRT to find the research sequence of this paper